Temperature Responsive Smart Textile

ABSTRACT

A textile fabric has at least one raised surface incorporating multicomponent fibers formed of at least a first polymer and a second polymer disposed in side-by-side relationship. The first polymer and the second polymer exhibit differential thermal elongation, which causes the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, thereby adjusting insulation performance of the textile fabric in response to ambient conditions.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. application Ser. No. 11/835,632, filed Aug. 8, 2007, now pending, which claims benefit from U.S. Provisional Patent Application 60/940,775, filed May 30, 2007, and U.S. Provisional Patent Application 60/840,813, filed Aug. 29, 2006. The entire disclosures of all of the aforementioned applications are incorporated herein by reference.

TECHNICAL FIELD

This invention relates to textile fabrics, and more particularly to textile fabrics responsive to changes in ambient temperature.

BACKGROUND

Standard textile fabrics have properties set during fabric construction that are maintained despite changes in ambient conditions and/or physical activity. These standard products are quite effective, especially when layered with other textile fabrics for synergistic effect and enhancement of comfort.

SUMMARY

Textile fabrics with raised surfaces, like fleece, either single face or double face, have different pile heights and different density for different ambient conditions and different activity.

According to one aspect, a textile fabric has at least one raised surface incorporating yarn comprising multicomponent fibers (e.g., bi-component fibers, tri-component fibers, etc.) formed of at least a first polymer and a second polymer disposed in side-by-side relationship. The first polymer and the second polymer exhibit differential thermal elongation (e.g., expansion and/or contraction), which causes the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, thereby adjusting insulation performance of the textile fabric in response to ambient conditions.

Preferred implementations may include one or more of the following additional features. At least one of the first polymer and the second polymer is a thermoplastic polymer with low glass transition temperature. The first polymer is a polypropylene and the second polymer is a polyethylene (e.g., linear low density polyethylene). The first polymer is a first polypropylene (e.g., an isotactic polypropylene) and the second polymer is a second polypropylene (e.g., a syndiotactic polypropylene) different from the first polypropylene. The multicomponent fibers may also include a third polypropylene different from both the first polypropylene and the second polypropylene. The yarn has a denier of about 90 to about 500, e.g., about 150 to about 360, e.g., about 160. The yarn has a tenacity of about 0.5 grams-force per denier to about 5.0 grams-force per denier, e.g., 0.9 grams-force per denier to about 2.4 grams-force per denier, e.g., about 2.3 grams-force per denier. The yarn has a filament count of 36 to 144. In some cases, for example, the yarn is a 72 filament yarn. The multicomponent fibers may have a round cross-section and the first polymer and the second polymer are arranged in a side-by-side configuration. The multicomponent fibers have a trilobal cross-section. The multicomponent fibers have a trilobal cross-section and the first polymer and the second polymer are arranged in a front-to-back configuration. The multicomponent fibers have a trilobal cross section and the first polymer and the second polymer are arranged in a left-to-right configuration. The multicomponent fibers have a delta cross-section. In some cases, the multicomponent fibers exhibit an overall average displacement of about −5% to about −60% over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.), e.g., about −11% to about −40% over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.), e.g., about −20% to about −40% over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.). The multicomponent fibers include extruded fibers (e.g., a pair of co-extruded fibers). The at least one raised surface is finished in a form selected from the group consisting of: fleece, velour, shearling, pile, and loop terry. The textile fabric has a knit construction (e.g., a circular knit construction, a single face knit construction, a double face knit construction, a weft knit construction, a warp knit construction, etc.). In some cases, the textile fabric is a pile fabric having woven or double needle bar Rachel warp knit construction.

In some examples, the second polymer is compatible with the first polymer. In some cases, the second material is a second polymer non-compatible with the first polymer. At least one of the first and second polymers is a thermoplastic polymer selected from polyester, polyurethane, polypropylene, polyethylene, and nylon. The first polymer is nylon and the second polymer is polyester. In some implementations, the multicomponent fibers also include a third polymer disposed between the first and second polymers. The third polymer is more compatible with both of the first and second polymers than the first and second polymers are with each other. The first and second polymers may include complementary interlocking surface features adapted to inhibit separation of the first and second materials. In some cases. the textile fabric has a technical face formed by a stitch yarn and a technical back formed by a loop and/or pile yarn. The loop and/or pile yarn includes the multicomponent fibers. The stitch yarn may include elastomeric yarn (e.g., spandex) for enhanced stretch and shape recovery. The differential thermal elongation of the first and second polymers is substantially reversible with low hysteresis. The adjustment to insulation performance of the textile fabric is substantially reversible with relatively low hysteresis. In some implementations, the textile fabric is incorporated in a temperature responsive textile fabric garment.

In another aspect, a textile fabric has at least one raised surface incorporating yarn including multicomponent fibers formed of at least a polypropylene and a polyethylene (e.g., about 50% polypropylene and about 50% polyethylene) disposed in side-by-side relationship. The polypropylene and the polyethylene exhibit differential thermal elongation, which causes the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, thereby adjusting insulation performance of the textile fabric in response to ambient conditions. The yarn has a denier of about 150 to about 160. The multicomponent fibers exhibit an overall average displacement of about −15% to about −40% (e.g., about −40%) over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.).

Preferred implementations may include one or more of the following additional features. The multicomponent fibers have a trilobal cross-section and the polypropylene and the polyethylene are arranged in a front-to-back configuration.

In a further aspect, a textile fabric has at least one raised surface incorporating multicomponent fibers (e.g., bi-component fibers, tri-component fibers, etc.) formed of at least a first material and a second material disposed (e.g., extruded, e.g., co-extruded) in side-by-side relationship. The first material and the second material exhibit differential thermal elongation (e.g., expansion and/or contraction), which causes the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, thereby adjusting insulation performance of the textile fabric in response to ambient conditions.

Preferred implementations may include one or more of the following additional features. The first material and the second material exhibit differential thermal elongation in response to changes in temperature over a predetermined range of temperature. Preferably, the predetermined range of temperature in 32° F. to 120° F. More preferably the predetermined range of temperature in 50° F. to 100° F. The raised surface is finished in a form selected from the group consisting of: fleece, velour, pile, shearling, and loop terry. The textile fabric has a knit construction selected from the group consisting of: circular knit construction, single face knit construction, double face knit construction, weft knit construction, and warp knit construction. The textile fabric is a pile fabric having woven or double needle bar Rachel warp knit construction. The multicomponent fibers include bi-component and/or tri-component fibers. The first material is a first polymer, and the second material is a second polymer compatible with the first polymer. The first and/or second material comprises a thermoplastic polymer selected from the group consisting of: polyester, polyurethane, and/or nylon. The first material is a first polymer (e.g., nylon), and the second material is a second polymer (e.g., polyester) non-compatible with the first polymer. The multicomponent fibers can also include a third polymer disposed between the first and second polymers. The third polymer may be more compatible with both of the first and second polymers than the first and second polymers are with each other. The first and second materials may include complementary interlocking surface features adapted to inhibit separation of the first and second materials. The fabric body has a technical face formed by a stitch yarn and a technical back formed by a loop and/or pile yarn including the multicomponent fibers. The thermal fabric can include elastomeric yarn (e.g., spandex such as Lycra®) incorporated in the stitch yarn for enhanced stretch and shape recovery. The differential thermal elongation of the first and second materials is substantially reversible with low hysteresis. The adjustment to insulation performance of the textile fabric is substantially reversible with relatively low hysteresis.

According to another aspect, a temperature responsive textile fabric garment includes a knit thermal fabric having a first raised surface, towards the wearer's skin, formed of one or more yarns made of multicomponent fibers. The multicomponent fibers include a first fiber component and a second fiber component arranged in a side-by-side configuration. The multicomponent fibers have differing thermal properties, which causes the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, thereby adjusting insulative properties of the textile fabric garment. Preferred implementations may include one or more of the following additional features. The knit thermal fabric includes a inner surface, towards the wearer's skin, having one or more regions of raised loop and/or pile yarn. The raised loop and/or pile yarn exhibits changes in bulk of between about 5% to about 50% over a temperature range of between about 32° F. and about 120° F. Preferably, the property of changing bulk as a function of ambient temperature changes is reversible with relatively low hysteresis. The multicomponent fibers exhibit changes in cross-sectional area from between about 5% to about 50% over a temperature range of between about 32° F. and about 120° F. The first and/or second fiber component may be a copolymer or a block polymer. The first and second fiber components may be secured together with physical anchoring. The first and second fiber components can include complementary interlocking surface features adapted to inhibit separation of the first and second materials. The multicomponent fibers include bi-component and/or tri-component fibers. The first fiber component includes a first polymer, and the second fiber component includes a second polymer compatible with the first polymer. The first fiber component includes a first polymer (e.g., polyester), and the second fiber component includes a second polymer (e.g., nylon) non-compatible with the first polymer. The multicomponent fibers can also include a third polymer disposed between the first and second fiber components. The third polymer is compatible with both of the first and second polymers. The multicomponent fibers may include an additive (e.g., silicate, zeolite, titanium dioxide, etc.) physically anchoring the first and second fiber components together. At least one of the first or second fiber components includes a serrated surface. The multicomponent fibers have one or more serrated surfaces. The multicomponent fibers have a substantially rectangular cross-sectional shape. The first and second fiber components have a substantially circular cross-sectional shape. The knit thermal fabric has a second raised surface, opposite the first raised surface, including one or more regions of raised loop and/or pile yarn. The second raised surface includes one or more yarns made of multicomponent fibers.

In yet another aspect, a method of forming a temperature sensitive textile fabric element for use in an engineered thermal fabric garment includes forming a continuous web of yarn and/or fibers including one or more multicomponent fibers. The method also includes finishing a first surface of the continuous web to form one or more regions of loop and/or pile yarn having a predetermined pile height and comprising the one or more multicomponent fibers. The multicomponent fibers are formed of at least a first material and a second material disposed in side-by-side relationship. The first material and the second material exhibit differential thermal elongation, which causes the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, thereby adjusting insulation performance of the textile fabric in response to ambient conditions.

Preferred implementations may include one or more of the following additional features. The method may also include finishing a second surface of the continuous web to form one or more other regions of loop and/or pile yarn comprising the multicomponent fibers. The step of forming the continuous web of yarn and/or fiber includes combining yarn and/or fibers by use of electronic needle and/or sinker selection. The step of finishing the first surface of the continuous web to form the one or more regions of loop and/or pile yarn having the predetermined pile height includes forming loops at the technical back of the textile fabric element. The step of forming the continuous web of yarn and/or fibers includes combining yarn and/or fibers, including the one or more multicomponent fibers, by tubular circular knitting. The step of forming the continuous web of yarn and/or fibers includes combining yarn and/or fibers, including the one or more multicomponent fibers, by reverse plating. The step of finishing the first surface includes finishing the first surface to form a single face fleece. The method may also include finishing a second surface of the continuous web to form a double face fleece. The step of forming the continuous web of yarn and/or fibers includes combining yarn and/or fibers, including the one or more multicomponent fibers, by plating. The step of forming the continuous web of yarn and/or fibers includes combining yarn and/or fibers, including the one or more multicomponent fibers, by regular plating; and wherein finishing the first surface further comprises finishing the first surface to form a single face fleece. The step of forming a continuous web of yarn and/or fibers comprises combining yarn and/or fibers, including the one or more multicomponent fibers, by warp knitting (e.g., double needle bar warp knitting, e.g., Raschel warp knitting). In one example, the step of forming a continuous web of yarn and/or fibers comprises combining yarn and/or fibers by Raschel warp knitting and the method includes cutting an interconnecting pile, thereby forming a single face cut pile fabric. In this case, the method may also include raising yarns forming a technical face of the cut pile fabric, thereby forming a double face fabric. The step of forming a continuous web of yarn and/or fibers comprises combining yarn and/or fibers, including the one or more multicomponent fibers, by sliver knitting. The step of finishing the first surface of the continuous web to form one or more regions of loop and/or pile yarn having the predetermined pile height includes raising the first surface. The method may include raising a second surface, opposite the first surface, of the continuous web. The method may also include cutting the loops of the one or more regions of loop and/or pile yarn, and finishing the cut loops to a common pile height. The first material and the second material exhibit differential thermal elongation, e.g., expansion and/or contraction, in response to changes in temperature over a predetermined range of temperature. Preferably, The predetermined range of temperature in 32° F. to 120° F., more preferably, in 50° F. and about 100° F. The method may also include combining the first material and the second material to form the one or more multicomponent fibers. Combining the first material and the second material may include co-extruding the first and second materials. The first and second materials are non-compatible polymers, and combing the first material and the second material may include co-extruding the first and second materials with a third polymer such that the third polymer is disposed between the first and second materials in the multicomponent fiber. The third polymer is compatible with both the first and second materials. Combining the first material and the second material may include physically anchoring the first material to the second material. Physically anchoring the first material to the second material may include adding an additive, such as silicate, zeolite, titanium dioxide, etc., to one or both the first and second materials, wherein the additive is operable bridge between the first and second materials physically or chemically. The first and/or second material may be selected from the group consisting of: polyester, polyurethane, and nylon The one or more regions of loop and/or pile yarn exhibit changes in bulk from between about 5% and about 50% over a temperature range of between about 50° F. and about 100° F. The one or more multicomponent fibers exhibit changes in cross-sectional area from between about 5% and about 50% over a temperature range of between about 50° F. and about 100° F.

The details of one or more embodiments of the invention are set forth in the accompanying drawings and the description below. Other features, objects, and advantages of the invention will be apparent from the description and drawings, and from the claims.

DESCRIPTION OF DRAWINGS

FIGS. 1A-1C are detailed views of a temperature responsive bi-component fiber.

FIGS. 2A-2B are cross-sectional views of temperature responsive smart textile fabric.

FIG. 3 is a perspective view of temperature responsive smart textile fabric garment.

FIGS. 3A-3C are detailed cross-sectional views of a temperature responsive smart textile fabric garment.

FIGS. 4A and 4B are detailed views of one embodiment of a temperature responsive bi-component fiber having a substantially rectangular cross-sectional shape.

FIG. 5 is a detailed view of a temperature responsive bi-component fiber having serrated surfaces.

FIGS. 6-9 illustrate various approaches for securing individual fiber components of a multicomponent fiber together.

FIG. 10 is a cross-section of a first sample yarn, sample yarn 1, a 144 filament formed of round, bi-component fibers consisting of polypropylene and polyethylene arranged in a side-by-side configuration.

FIG. 11 shows photographs, of a multicomponent fiber undergoing a thermal displacement test.

FIG. 12 is a graphical depiction of thermal displacement test results obtained for test fibers of sample yarn 1.

FIG. 13 is a cross-section of a second sample yarn, sample yarn 2, a 72 filament yarn formed of trilobal, bi-component fibers consisting of polypropylene and polyethylene arranged in a front-to-back configuration.

FIG. 14 is a graphical depiction of thermal displacement test results obtained for test fibers of sample yarn 2.

FIG. 15 is a graphical depiction of thermal displacement test results obtained for test fibers of a third sample yarn, sample yarn 3, a 144 filament yarn formed of trilobal, bi-component fibers consisting of polypropylene and polyethylene arranged in a front-to-back configuration.

FIG. 16 is a cross-section of a 72 filament yarn formed of trilobal, bi-component fibers consisting of polypropylene and polyethylene arranged in a left-to-right configuration.

FIG. 17 is a cross-section of a 72 filament yarn formed of bi-component fibers having a rectangular shape and consisting of polypropylene and polyethylene arranged in a side-by-side configuration.

FIG. 18 is a detailed view of a temperature responsive bi-component fiber.

Like reference symbols in the various drawings indicate like elements.

DETAILED DESCRIPTION

FIG. 1A is a detailed view of a bi-component fiber 10. Fiber component 10 includes two temperature responsive materials, i.e., first and second fiber components A, B arranged in side-by-side relationship. The first and second fiber components A, B exhibit differential thermal elongation, e.g., expansion and or contraction, in response to changes in temperature. As result, the fiber has a tendency to bend and/or curl in response to ambient conditions. Suitable materials for the first and/or second fiber components A, B include polyester, polyurethane, and nylon.

For example, in one embodiment, the first fiber component A has a relatively greater coefficient of thermal expansion (i.e., a greater propensity to grow and/or expand in response to an increase in temperature) than the second fiber component B. When the fiber 10 is exposed to heat over a critical temperature range, the first fiber component A expands at a relatively greater rate than the second fiber component B causing the fiber to bend (see, e.g., FIG. 1B). If the differential elongation (e.g., expansion and/or shrinkage) exceeds a certain threshold level the fiber 10 will tend to curl (see, e.g., FIG. 1C). This process is also reversible with low hysteresis; i.e., the fiber 10 will return toward its original three dimensional configuration once the temperature returns below the critical temperature range. Suitable bi-component fibers of this type are produced by Mide Technologies Corporation of Medford, Mass.

FIG. 2A illustrates a temperature responsive textile fabric 20 including a raised surface of bi-component fibers 10 of the kind described above. The fabric 20 includes a generally sheet-form base 22, preferably of knit construction, having at least one raised surface 24 (e.g., pile yarn in warp knit or special circular knit) including a bi-component fiber 10 (e.g., as a sinker loop yarn, or pile). Yarns formed of the fibers 10 can have a denier of about 90 to about 500, e.g., about 150 to about 360. Yarns formed of the fibers 10 can have a tenacity of about 0.5 grams-force per denier to about 5.0 grams-force per denier, e.g., about 2.3 grams-force per denier. Change in thermal insulation of the textile fabric 20 is a result of change in the bulk/thickness of pile yarn forming the raised surface when the pile yarn is made of bi-component fibers 10 and exposed to different temperatures.

In any of the foregoing knit constructions, elastomeric yarn may be added (e.g., spandex such as Lycra®) to, e.g., the stitch yarn. For example, in some cases, spandex is incorporated in the stitch yarn for enhanced stretch and shape recovery. As the ambient temperature is increased, the fibers of the raised surface(s) begin to bend and/or curl toward the surface changing the loft and density of the fabric, and, as a result, adjust the insulation performance of the fabric 20. FIG. 2B illustrates the behavioral response of a double face temperature responsive textile fabric.

In one example, as shown in FIG. 3, the temperature responsive textile fabric 20 can be incorporated in a fabric garment 30. As illustrated in FIG. 3A, the raised surface 24, including the bi-component fibers 10, contacts the user's skin S providing enhanced comfort, water management, and enhanced air movement and ventilation. As the ambient temperature increases, the fibers of the raised surface begin to bend (FIG. 3B) and curl (FIG. 3C) changing the three dimensional configuration of the fabric, thereby modifying the thermal insulation of the garment; i.e., as the ambient temperature increases the fabric gets thinner (less loft), therefore less insulation, providing enhanced overall comfort.

Preferably, the changes in three dimensional configuration occur over a temperature range of between about 32° F. and about 120° F., more preferably, between about 50° F. and about 100° F.

A number of embodiments of the invention have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the invention. For example, the bi-component fibers may have a variety of cross-sectional shapes. FIG. 4A, for example, illustrates one embodiment of a bi-component fiber 40 having a substantially rectangular cross-section with long sides 43, 44 and short sides 45, 46. The bi-component fiber 40 includes two different polymers, i.e., first and second fiber components 41, 42 arranged in side-by-side relation, which exhibit differential thermal elongation, e.g., expansion and/or contraction, in response to changes in temperature. In this example, the first fiber component 41 has a relatively greater coefficient of thermal expansion than the second fiber component 42. Thus, as with the bi-component fibers described above (e.g., with regard to FIGS. 1A-1C), when the fiber 40 is exposed to heat over a critical temperature range, the first fiber component 41 expands at a relatively greater rate than the second fiber component 42 causing the fiber to bend (see, e.g., FIG. 4A), and, if and/or when the differential elongation (e.g., expansion and/or contraction (shrinkage)) exceeds a certain threshold, the fiber 40 will tend to curl (see, e.g., FIG. 4B). Due to the substantially rectangular cross-sectional shape, the bi-component fiber 40 will tend to bend relatively easily along the long sides 43, 44 (as indicated by arrow 47 in FIG. 4A), e.g., as compared to the short sides 45, 46. This process is also reversible with low hysteresis; i.e., the fiber 40 will return toward its original three dimensional configuration once the temperature returns below the critical temperature range.

The bi-component fibers can have plain surfaces and/or one or more serrated surfaces. For example, FIG. 5 illustrates a bi-component fiber 50 that includes first and second fiber components 51, 52 having serrated surfaces 53, 54. The serrated surfaces can provide a different visual appearance, tactile properties, toughness, and/or light reflectance, e.g., as compared to the plain surfaces illustrated in FIGS. 1A and 4A.

In some embodiments, the bi-component fiber can include two non-compatible polymers (i.e., fiber components) or polymers with poor compatibility such as nylon and polyester. For example, in some cases the bi-component fiber may include nylon and polyester fibers disposed in side-by-side relationship. Fibers formed with non-compatible polymers or polymers with poor compatibility may exhibit a tendency to split; i.e., the individual fiber components may exhibit a tendency to separate, which can alter the effects of the bi-component response to changes in temperature.

FIGS. 6 and 7 illustrate an approach for inhibiting separation of individual fiber components of a multicomponent fiber. FIG. 6 illustrates the approach as applied to a tri-component fiber 60 that includes first and second fiber components 61, 62 having substantially circular cross-sections. As shown in FIG. 6, a third polymer 63 is disposed between (e.g., co-extruded with) the first and second polymers (i.e., first and second fiber components 61, 62). The third polymer 63 is used as a bridge to aid in securing the first and second polymers together. The third “bridge” polymer 63 can be more compatible with each of the first and second polymers than the first and second polymer are with each other, thereby providing a stronger bond between the first and second polymers and reducing the likelihood of separation.

FIG. 7 illustrates the approach described above with regard to FIG. 6, as applied to a tri-component fiber 70 that includes first and second fiber components 71, 72 having substantially rectangular cross-sections with serrated surfaces 73, 74. As shown in FIG. 7 a third polymer 75 is used as a bridge to secure non-compatible polymers of first and second fibers components 71, 72.

FIGS. 8 and 9 illustrate another approach for inhibiting separation of individual fiber components of a multicomponent fiber, in which the individual fiber components are secured together by physical anchoring. This approach may be used alone or in combination with the approach described above with regard to FIGS. 7 and 8. The physical anchoring can be achieved by providing different, interlocking shapes along mating surfaces at the interface of the fiber components. For example, as shown in FIG. 8, mating surfaces of the first and second fiber components 81, 82 are provided with complementary interlocking features 83, 84 which operate to anchor the first and second polymers together. Alternatively or additionally, as shown for example in FIG. 9, physical anchoring can be achieved by adding an additive 93 (such as silicate, zeolite, titanium dioxide (TiO₂), etc.), which will physically or chemically bridge between first and second fiber components 91, 92 of a multicomponent fiber 90, thereby anchoring the fiber components 91, 92 together.

In some embodiments, a temperature responsive textile fabric, such as the temperature responsive smart textile fabric of FIGS. 2A and 2B, suitable for use in a fabric garment, such as the garment described above with reference to FIG. 3, can incorporate yarns that include bi-component fibers consisting of propylene and polyethylene (e.g., linear low density polyethylene (LLDPE)). Yarns formed of the bi-component fibers can have a denier of about 90 to about 500, e.g., about 150 to about 360. Yarns formed of the bi-component fibers can have a tenacity of about 0.5 grams-force per denier to about 5.0 grams-force per denier, e.g., about 2.3 grams-force per denier. Change in thermal insulation of the textile fabric/fabric garment is a result of change in the bulk/thickness of the pile yarn when the pile yarn is made of bi-component fibers and exposed to different temperatures.

Table 1 shows a number of sample yarns that were each formed of bi-component fibers consisting of a first polymer (PH-835 polypropylene, manufactured by Basell Canada Inc., Corunna, Ontario, sold under the trademark Pro-fax™ PH835 described in Material Safety Data Sheet PH835 of Basell, Issue Date: Mar. 28, 2000, Revision No.: New MSDS, the entire disclosure of which is incorporated herein by reference) and a second polymer (linear low density polyethelene, e.g., 8335 NT-7 LLDPE available from The Dow Chemical Company, Midland, Mich. and described in Material Safety Data Sheet 22539/1001 of Dow Chemical Company, Issue Date: Sep. 18, 2008, Version: 2.2, the entire disclosure of which is incorporated herein by reference) at a 50/50 ratio.

TABLE 1 Filament Average Sample Polymer Polymer Material Cross Draw Average Average Tenacity Yarn # A B Ratio Section Ratio Denier Elongation gpd 1 PH-835 8335 50/50 144   4:1 320.3 101% 2.39 PP NT-7 RND S/S LLDPE 2 PH-835 8335 50/50 72 TRI 3.50:1 159.7 111% 2.28 PP NT-7 F/B LLDPE 3 PH-835 8335 50/50 144 TRI  3.5:1 317.7 118% 2.24 PP NT-7 F/B LLDPE

Referring to Table 1, sample yarn 1 was a 144 filament yarn. Sample yarn 1 had an average denier of 320.3, exhibited an average elongation of 101%, and had an average tenacity of 2.39 grams-force per denier (gpd). As shown in FIG. 10, the filaments of sample yarn 1 have a round (RND) cross-section, in which the first and second polymers had been co-extruded in a side-by-side (S/S) configuration.

A total of four single fiber thermal displacement tests were run on test fibers of sample yarn 1. FIG. 11 shows photographs, of a fiber under test, from an exemplary thermal displacement test. The top two images are front and side views (on the left and right hand side of the page, respectively) of a fiber under test at the starting temperature of −30° C. (−22° F.). As shown in FIG. 11, at −30° C. the individual fiber is in a substantially vertical orientation. As the temperature is increased to 0° C. (32° F.), the loft (i.e., the height of the fiber in the vertical direction) decreases, as shown in the middle two images of FIG. 11. The loft of the fiber under test continues to decrease as the temperature is increased to +35° C. (95° F.), as shown in the bottom two images of FIG. 11.

FIG. 12 is a graphical depiction of the test results obtained for the test fibers of sample yarn 1. FIG. 12 shows the % Average Displacement as a function of Dwell Temperature for each of the four single fiber thermal displacements tests for sample yarn 1, as well as an overall computed average. The % Average Displacement is calculated by determining a % change in height (loft) H1 (see, e.g., FIG. 11) for the front view of the fiber under test and a % change in height (loft) H2 (see, e.g., FIG. 11) for a side view of the fiber under test and then taking an average of those two values. As shown in FIG. 12, the fiber of sample yarn 1 exhibited an overall average displacement of −15% over the temperature range of −30° C. (−22° F.) to +35° C. (95° F.). Identical tests were conducted for sample yarns 2 and 3.

Sample yarn 2 was a 72 filament yarn. Sample yarn 2 had an average denier of 159.7, exhibited an average elongation of 111%, and had an average tenacity of 2.28 grams-force per denier (gpd). As shown in FIG. 13, the filaments of sample yarn 2 have a trilobal (TRI) cross-section, in which the first and second polymers (PH-835 PP and 8335 NT-7 LLDPE, respectively) had been co-extruded, side-by-side, in a front-to-back (F/B) configuration.

A total of four single fiber thermal displacement tests were also run on test fibers of sample yarn 2. FIG. 14 depicts the test results obtained. FIG. 14 shows the % Average Displacement as a function of Dwell Temperature for the fiber of sample yarn 2 for each of the four single fiber thermal displacements tests, as well as an overall computed average. The fibers of sample yarn 2 exhibited a decrease in height with increasing temperatures. As shown in FIG. 14, the fiber of sample yarn 2 exhibited an overall average displacement of −40% over the temperature range of −30° C. (−22° F.) to +35° C. (95° F.).

Sample yarn 3 was a 144 filament yarn having a trilobal cross-section in which the first and second polymers (PH-835 PP and 8335 NT-7 LLDPE, respectively) have been co-extruded, side-by-side, in a front-to-back (F/B) configuration. Sample yarn 3 had an average denier of 317.7, exhibited an average elongation of 118%, and had an average tenacity of 2.24.

A total of four single fiber thermal displacement tests were run on an individual filament of sample yarn 3. FIG. 15 depicts the test results obtained. FIG. 15 shows the % Average Displacement as a function of Dwell Temperature for the fiber of sample yarn 3 for each of the four single fiber thermal displacements tests. The fiber of sample yarn 3 also exhibited a decrease in height with increasing temperatures. As shown in FIG. 15, the fiber of sample yarn 3 exhibited an overall average displacement of −12% over the temperature range of −30° C. (−22° F.) to +35° C. (95° F.).

FIG. 16 shows another embodiment of a 72 filament yarn having filaments with a trilobal cross-section. In the individual filaments shown in FIG. 16, the first and second polymers (PH-835 PP and 8335 NT-7 LLDPE, respectively) have been co-extruded side-by-side, in a left-to-right (L/R) configuration.

Other suitable polypropylenes include 360H PP, available from Braskem PP Americas, Inc, and described in Material Safety Data Sheet CP360H Homopolymer Polypropylene published by Sunoco Chemical, Revision Date: Mar. 26, 2008, which references Material Safety Data Sheet code number C4001 published by Sunoco Chemicals, dated Jan. 25, 2006, the entire disclosure of both of these Material Safety Data Sheets are incorporated herein by reference).

Other fiber cross-sections are also possible. For example, FIG. 17 shows a component yarn that include bi-component fibers (polypropylene/polyethylene) having a rectangular cross-section. Other fibers may have a delta cross-section. In some case, for example, yarns may include fibers (e.g., multi-component fibers) having different, relative cross-sectional shapes. For example, some yarns may include round fibers and tri-lobal fibers.

In some embodiments, a temperature responsive textile fabric, suitable for use in a fabric garment, can incorporate yarns that include tri-component fibers consisting of three types of propylene (e.g., Isotactic polypropylene (iPP), Syndiotactic polypropylene (sPP), and Polypropylene PP).

While yarns comprising fibers of various cross-sectional shapes have been described other shapes are possible. For example, FIG. 18 illustrates an exemplary fiber having a delta cross-section, which can be incorporated into a multifilament yarn. As shown in FIG. 18, the fiber 100 includes a first polymer 102 and a second polymer 104 extruded in side-by-side configuration.

In some implementations, the textile fabric may be produced by any procedure suitable for combining yarns and/or fibers to create a finished fabric having at least one raised surface. The first and second materials of the multicomponent fibers can exhibit differential elongation in response to changes in relative humidity, or changes in level of liquid sweat (e.g., where the temperature responsive fabric is incorporated in a garment). The raised surface can be finished as fleece, velour, pile and/or terry loop. The temperature responsive textile fabric can be incorporated in an insulative layer in a multi-layer garment system. Accordingly, other embodiments are within the scope of the following claims. 

1. Textile fabric having at least one raised surface incorporating yarn comprising multicomponent fibers formed of at least a first polymer and a second polymer disposed in side-by-side relationship, the first polymer and the second polymer exhibiting differential thermal elongation to cause the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, adjusting insulation performance of the textile fabric in response to ambient conditions.
 2. The textile fabric of claim 1, wherein at least one of the first polymer and the second polymer comprises a first thermoplastic polymer with low glass transition temperature.
 3. The textile fabric of claim 1, wherein the first polymer is a polypropylene and the second polymer is a polyethylene
 4. The textile fabric of claim 3, wherein the polyethylene is linear low density polyethylene.
 5. The textile fabric of claim 1, wherein the first polymer is a first polypropylene and the second polymer is a second polypropylene different from the first polypropylene.
 6. The textile fabric of claim 5, wherein the first polypropylene is an isotactic polypropylene and the second polypropylene is a syndiotactic polypropylene.
 7. The textile fabric of claim 5, wherein the multicomponent fibers further comprise a third polypropylene different from both the first polypropylene and the second polypropylene.
 8. The textile fabric of claim 1, wherein the yarn has a denier of about 90 and to about
 500. 9. The textile fabric of claim 8, wherein the yarn has a denier of about
 160. 10. The textile fabric of claim 1, wherein the yarn has a tenacity of about 0.5 grams-force per denier to about 5.0 grams-force per denier.
 11. The textile fabric of claim 10, wherein the yarn has a tenacity of about 2.3 grams-force per denier.
 12. The textile fabric of claim 1, wherein the yarn has a filament count of 36 to
 144. 13. The textile fabric of claim 12, wherein the yarn is a 72 filament yarn.
 14. The textile fabric of claim 1, wherein the multicomponent fibers have a round cross-section and the first polymer and the second polymer are arranged in a side-by-side configuration.
 15. The textile fabric of claim 1, wherein the multicomponent fibers have a rectangular cross-section and the first polymer and the second polymer are arranged in a side-by-side configuration.
 16. The textile fabric of claim 1, wherein the multicomponent fibers have a trilobal cross-section.
 17. The textile fabric of claim 16, the multicomponent fibers have a trilobal cross-section and the first polymer and the second polymer are arranged in a front-to-back configuration.
 18. The textile fabric of claim 16, wherein the wherein the multicomponent fibers have a trilobal cross section and the first polymer and the second polymer are arranged in a left-to-right configuration.
 19. The textile fabric of claim 1, wherein the multicomponent fibers have a delta cross-section.
 20. The textile fabric of claim 1, wherein the multicomponent fibers exhibit an overall average displacement of about −5% to about −60% over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.).
 21. The textile fabric of claim 20, wherein the multicomponent fibers exhibit an overall average displacement of about −20% to about −40% over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.)
 22. Textile fabric having at least one raised surface incorporating yarn comprising multicomponent fibers formed of at least a polypropylene and a polyethylene disposed in side-by-side relationship, the polypropylene and the polyethylene exhibiting differential thermal elongation to cause the multicomponent fibers to bend or curl and reversibly recover in response to changes in temperature, adjusting insulation performance of the textile fabric in response to ambient conditions, wherein the yarn has a denier of about 150 to about 160, and wherein the multicomponent fibers exhibit an overall average displacement of about −5% to about −60% over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.).
 23. The textile fabric of claim 22, wherein the multicomponent fibers exhibit an overall average displacement of −20% to about −40% over a temperature range of from −22° F. (−30° C.) to 95° F. (+35° C.).
 24. The textile fabric of claim 22, wherein the multicomponent fibers have a trilobal cross-section and the polypropylene and the polyethylene are arranged in a front-to-back configuration.
 25. The textile fabric of claim 22, wherein the multicomponent fibers consist of about 50% polypropylene and about 50% polyethylene.
 26. A temperature responsive textile fabric garment, comprising the textile fabric of claim 1 or claim
 22. 